Viprene™ P45D-22U-BLK
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Alliance Polymers & Services |
| Trademark: | Viprene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ewc1Dr_Viprene-P45D-22U-BLK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Viprene™ P45D-22U-BLK is a UV and Heat Stabilized TPV (thermoplastic vulcanizate elastomer). This material can be easily procesed by extrusion or injection molding. It exhibits easy flowing characteristics. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A | 95 | ||
| Shore D | 45 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% Strain | 8.60 | MPa | |
| 300% Strain | 11.8 | MPa | |
| Tensile Stress (Break) | 15.5 | MPa | ISO 37 |
| Tensile Elongation (Break) | 500 | % | ISO 37 |
| Tear Strength | 90 | kN/m | ISO 34-1 |
| Compression Set (70°C, 22 hr) | 40 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2590F | Teknor Apex Company | TPE | Telcar® |
| Vydyne® ECO315 BK06 | Ascend Performance Materials Operations LLC | Nylon 66/6 | Vydyne® |
| DI-COAT R-4721/7 | Hapco Inc. | TP, Unspecified | DI-COAT |
| Grivory® HTM-4H1 | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| OnForce™ LFT LF5200-5007 BLACK UV | PolyOne Corporation | PP Homopolymer | OnForce™ LFT |