Ultramid® A3EG6 FC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EwFcC7_Ultramid-A3EG6-FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The BASF Ultramid® FC (Food Contact) grades enable the industry to develop products for food contact applications which are in compliance with multiple regional food contact regulations including FDA, European Food Contact n°2002/72/EC and GMP (EC) n°2023/2006. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 40.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.2 to 5.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.5 to 1.9 | -- | % | |
| Viscosity Number (96% H2SO4 (Sulphuric Acid)) | 145 | -- | cm³/g | ISO 307 |
| Mold Shrinkage - constrained 1 | 0.55 | -- | % |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Maximum Service Temperature - short cycle operation | 240 | -- | °C | |
| Temperature Index - at 50% loss of tensile strength | IEC 60216 | |||
| -- 2 | 165 | -- | °C | |
| -- 3 | 135 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Passed | -- | FMVSS 302 | |
| Polymer Abbreviation | PA66-GF30 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 190 | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 5.0 | % | ISO 527-2 |
| Tensile Creep Modulus 4(1000 hr) | -- | 5300 | MPa | ISO 899-1 |
| Flexural Modulus | 8600 | 6500 | MPa | ISO 178 |
| Flexural Stress | 280 | 210 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | -- | kJ/m² | |
| 23°C | 13 | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | -- | kJ/m² | |
| 23°C | 85 | 100 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 12 | 16 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 80°C | 2.0E-5 to 3.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 80°C | 6.0E-5 to 7.0E-5 | -- | cm/cm/°C | |
| Specific Heat | 1500 | -- | J/kg/°C | |
| Thermal Conductivity | 0.35 | -- | W/m/K | DIN 52612 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.50 | 5.60 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.014 | 0.16 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test box with central gating, dimensions of base (107*47*1,5) mm, processing conditions: TM = 290°C, TW = 80°C |
| 2 . | 5000 h |
| 3 . | 20000 h |
| 4 . | strain <= 0.5%, 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Daelim Po1y® 5502-03LD | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Daelim Po1y® LL-04S | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| Esmedica VH 9142EH | Sekisui Chemical Company, Ltd. | PVC, Unspecified | Esmedica VH |
| ESPREE™ ABS10GF | SABIC Innovative Plastics | ABS | ESPREE™ |
| Durethan® C 38 FA 000000 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |