SABIC® HDPE B5260LS
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EwFO32_SABIC-HDPE-B5260LS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE B5260LS exhibits good processing properties, typically on high speed extrusion blow moulding machines for UHT milk bottles. Its broad molecular weight distribution offers typically good behaviour during extrusion and blowing, and it is typically used for multi- and mono-layer constructions. Furthermore it has good organoleptic properties, which are required in for example the packaging of dairy products, such as sterilized milk. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 2.0 | g/10 min | |
| 190°C/21.6 kg | 60 | g/10 min | |
| 190°C/5.0 kg | 7.0 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, Compression Molded, F50) | 10.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1100 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 26.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 31.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 200 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1150 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 26.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Compression Molded) | 7.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 124 | °C | ISO 306/A |
| Melting Temperature (DSC) | 131 | °C | ISO 11357-3 |
| Enthalpy Change | 202 | J/g | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP HRV140 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| NatureFlex™ 28NP | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| FRblend® PA66-1301 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Nylon 66 | FRblend® |
| HAIPLEN H30 G8 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| DOW™ Electrical & Telecommunications HFDK-4201 NT | The Dow Chemical Company | PE, Unspecified | DOW™ Electrical & Telecommunications |