ASTABLEND™ MNM19
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTABLEND™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EvpMQ5_ASTABLEND-MNM19.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTABLEND™ MNM19 is an UV stabilized ABS/PA blend with very high impact strength. The grade features excellent melt flow properties resulting in outstanding processability and superb surface finish. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.07 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (240°C/10.0 kg) | 30.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (4.00 mm) | 2000 | 1600 | MPa | ISO 527-2/50 |
| Tensile Stress (4.00 mm) | 43.0 | 34.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield, 4.00 mm | 3.0 | -- | % | |
| Break, 4.00 mm | 28 | -- | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 16 | -- | kJ/m² | |
| 23°C | 71 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, Unannealed | 98.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 180 | 106 | °C | ISO 306/B50 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 245 to 255 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 245 to 265 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 60.0 to 120 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 50 | rpm | |
| Clamp Tonnage | 3.0 to 5.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 10.0 x 4.0 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4065 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 289 TFE 10 | RTP Company | Nylon 66 | RTP |
| Zhongfa PP pp5 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| KYOCERA KE-880 | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| Sylvin 4299-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |