G-Blend 85 PC/ABS
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Gardiner Compounds Ltd. |
| Trademark: | G-Blend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ev9urP_G-Blend-85-PC-ABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
G-Blend 65/85/85HI is a non-reinforced, amorphous thermoplastic polymer blend based on polycarbonate and acrylonitrile butadiene styrene. It is noted for its toughness, rigidity and ability to flow and mould easily. This blend contains a proportion of recycled and prime material to produce a polymer that offers outstanding properties, giving users the benefit of considerable cost down over equivalent prime grades. G-Blend 65/85/85HI complies with all the recycling directives and can be recycled in the normal way. Typical applications include interior automotive trim, mobile phone housings, electrical and electronic enclosures and some household goods. This material is available in a black and natural and a whole range of colours. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 0.50 - 0.70 | % | ISO 2577 |
| Water Absorption (equilibrium, 23°C, 85% RH) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 53.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 110 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 245 - 265 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 70.0 - 100 | °C |
| Injection instructions |
|---|
| Max Dwell Time: 8 mins |
| Note Message | |
|---|---|
| 1 . | 500 bar |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PP ZC011 | Borealis AG | TPO | Borealis PP |
| Apec® 1797 | Covestro - Polycarbonates | PC | Apec® |
| Halene P B202S | Haldia Petrochemicals Ltd. | PP Random Copolymer | Halene P |
| Kingfa PP-1016 | Kingfa | PP, Unspecified | Kingfa |
| Sylvin 4200-88 White 1523 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |