RTP VLF 80207 EM HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EuiHSG_RTP-VLF-80207-EM-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Long Glass Fiber - Easy Molding - Heat Stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.30 | % | ASTM D955 |
| Moisture Content | 0.20 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13800 | MPa | ASTM D638 |
| Tensile Strength | 228 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 - 3.0 | % | ASTM D638 |
| Flexural Modulus | 12100 | MPa | ASTM D790 |
| Flexural Strength | 345 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 350 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 1300 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 254 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 271 - 299 | °C | |
| Mold Temperature | 65.6 - 124 | °C | |
| Injection Pressure | 34.5 - 124 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TP8LDZ (Series: UV/LD/b) | KRAIBURG TPE | TPE | THERMOLAST® K |
| TOTAL Polypropylene PPH 3230XZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| CYCOLAC™ MG37EPX resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Durepol® PBT A3 G15 TZ NTLA010 BT327 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| LUVOCOM® 20-0951 | Lehmann & Voss & Co. | PPA | LUVOCOM® |