Geon™ Vinyl Dry Blend E7506
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Dry Blend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EtgG72_Geon-Vinyl-Dry-Blend-E7506.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon E7506 is recommended for whites and light pastel colors only. Performs well in high rate fencing capstock applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 16354 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2920 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 43.4 | MPa | ASTM D638 |
| Flexural Modulus | 3150 | MPa | ASTM D790 |
| Flexural Strength | 84.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 110 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 57.4 | J/cm | ASTM D4226 |
| 23°C 4 | 60.1 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 3.18mm 5 | 80.0 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm 6 | 77.5 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 7 | 78.3 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 8 | 75.9 | °C | ASTM D648 |
| CLTE - Flow | 6.1E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Physical properties based on Geon E7506 white 1880. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| 5 . | Annealed at 60 deg.C |
| 6 . | conditioned @ 50 deg.C |
| 7 . | Annealed at 60 deg.C |
| 8 . | Conditioned at 50 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3880H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| POYAD WA202 | Pooya Polymer Tehran | PE, Unspecified | POYAD |
| MORETEC™ 0138N | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| VESTAMID® D DX9322 | Evonik Industries AG | Nylon 612 | VESTAMID® D |
| PSM® HL-101-40 | Wuhan Huali Environmental Technology Co., Ltd. | TP, Unspecified | PSM® |