Novamid® 1013C
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Novamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EsMM6A_Novamid-1013C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Novamid® 1013C is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific for injection molding. Important attributes of Novamid® 1013C are:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 1.2 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.8 | -- | % | ISO 62 |
| Viscosity Number | 138 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 83.0 | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.3 | -- | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 20 | -- | % | ISO 527-2 |
| Flexural Modulus | 3000 | 990 | MPa | ISO 178 |
| Flexural Stress | 119 | 40.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | 31 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 175 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 57.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 6.0E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 2.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 26 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.00 | -- | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.022 | -- | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | V-2 | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 275 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan 2000/B-8580 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Adiprene® Duracast® SE940 | Chemtura | PUR-Est/eth,MDI | Adiprene® Duracast® |
| Elastamax™ XL-1035-21-8001 Black | PolyOne Corporation | SBC | Elastamax™ |
| LONGLITE® PMC T 385J | CCP Group | Phenolic | LONGLITE® PMC |
| Sylvin 83043-75FUV Grey 9518 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |