Makrolon® SF810
| Category: | PC , Polycarbonate |
| Manufacturer: | Covestro - Polycarbonates |
| Trademark: | Makrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EqX8p3_Makrolon-SF810.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MVR (300 °C/1.2 kg) 6.0 cm³/10 min; structural foam; glass fiber reinforced; flame retardant; easy release; injection molding; in combination with an appropriate blowing agent for the production of structural foam moldings |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.27 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.45 | % | |
| Flow : 2.00 mm | 0.60 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.26 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3800 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield, 23°C | 64.0 | MPa | ISO 527-2/50 |
| Break, 23°C | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield, 23°C | 4.0 | % | ISO 527-2/50 |
| Break, 23°C | 15 | % | ISO 527-2/5 |
| Flexural Modulus 2(23°C) | 3600 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 105 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 4(23°C) | 5.8 | % | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 135 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 6.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 36 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.20 | ||
| 23°C, 1 MHz | 3.20 | ||
| Comparative Tracking Index (Solution A) | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index 5 | 35 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 60x60x2 mm |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2 mm/min |
| 5 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SilTRUST® E110 | Momentive Performance Materials Inc. | Silicone | SilTRUST® |
| TRANSMARE® 10HGF30-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| NuSil CV3-2640 | NuSil Technology | Silicone | NuSil |
| EL-Lene™ H6140B | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| HIPLEX® HXM 45060 | HIP-PetroHemija | HDPE | HIPLEX® |