TECHNYL® C 218 V33 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eps1PZ_TECHNYL-C-218-V33-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide PA6, reinforced with 33% of glass fibre, heat stabilized, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.37 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.92 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10200 | 6620 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 193 | 113 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.1 | 4.2 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9660 | 6040 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | 32 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 15 | 26 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 222 | -- | °C | ISO 3146 |
| CLTE - Flow (23 to 85°C) | 2.9E-5 | -- | cm/cm/°C | ASTM E831 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength (23°C) | -- | 22 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C, 1 MHz) | 3.80 | 4.50 | IEC 60250 | |
| Dissipation Factor (23°C, 1 MHz) | 0.020 | 0.090 | IEC 60250 | |
| Comparative Tracking Index | 550 | 475 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 225 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan A-9007/B-6088 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Alathon® L4903 | LyondellBasell Industries | HDPE, HMW | Alathon® |
| CPI PA6 40 Natural | CPI Binani, Inc. | Nylon 6 | CPI PA6 |
| Diamond HIPS HI-851 | Diamond Polystyrene | PS (HIPS) | Diamond HIPS |
| Hifax ERC 347P G14008 | LyondellBasell Industries | PP Copolymer | Hifax |