DIALAC® KD102S
| Category: | AES , Acrylonitrile Ethylene Styrene |
| Manufacturer: | UMG ABS, Ltd. |
| Trademark: | DIALAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Epa3pO_DIALAC-KD102S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DIALAC® KD102S is an Acrylonitrile Ethylene Styrene (AES) material. It is available in Asia Pacific or North America for injection molding. Important attributes of DIALAC® KD102S are:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 110 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.60 to 0.80 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 107 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2350 | MPa | ISO 527-2 |
| Tensile Stress (23°C) | 45.0 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 61.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 72.0 | °C | ISO 75-2/Af |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 3.00 mm | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 6.0 | hr | |
| Rear Temperature | 150 to 190 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 180 to 220 | °C | |
| Nozzle Temperature | 170 to 210 | °C | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Pressure | 70.0 to 130 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 5.00 to 10.0 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3589 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TAIRISAN NF2200 | Formosa Plastics Corporation | SAN | TAIRISAN |
| TOTAL Polypropylene PPC 9612 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Bergamid™ NN-33GF/000 BLACK | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Generic Nylon 6 - Glass\Carbon Fiber | Generic | Nylon 6 | Generic |