Kepex® 3300SC
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eoymf0_Kepex-3300SC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KEPEX 3300SC is an unfilled, impact modified, and high melt flow PBT. It exhibits good toughness and impact strength. It is applicable to automotive, electrical, electronic, and industrial parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.8 to 2.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 51.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 150 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2210 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 75.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 150 | °C | |
| 1.8 MPa, Unannealed | 50.0 | °C | |
| Melting Temperature | 220 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 230 to 250 | °C | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuang-Bang AB-109K | Shuang-Bang Industrial Corp. | PUR, Unspecified | Shuang-Bang |
| Tarnamid® T- 27 MCS I | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Daelim Po1y® PH-630 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| ENVIROPLAS® ENV08-NC470 | ENVIROPLAS®, Inc. | PBT | ENVIROPLAS® |
| Softell TKG 300N C12453 | LyondellBasell Industries | PP Copolymer | Softell |