RTP VLF 84709
| Category: | PTT , Polytrimethylene Terephthalate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eom1Ii_RTP-VLF-84709.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
"Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade." |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 - 0.30 | % | ASTM D955 |
| Moisture Content | 0.010 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15900 | MPa | ASTM D638 |
| Tensile Strength | 152 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.0 - 2.0 | % | ASTM D638 |
| Flexural Modulus | 16500 | MPa | ASTM D790 |
| Flexural Strength | 228 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 190 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 640 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 207 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 127 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | -40.0 | °C | |
| Processing (Melt) Temp | 232 - 260 | °C | |
| Mold Temperature | 87.8 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 -Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® CA RV300L 100 NAT | Radici Plastics | Nylon 66/6 | Radilon® |
| Xuchuan XCW-9021 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Grivory® GV-2 FWA nat | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Lusep® SP2300 | LG Chem Ltd. | SPS | Lusep® |
| Hifax TRS 260P C11319 | LyondellBasell Industries | PP Copolymer | Hifax |