Manner Flexible PVC V969 NAT601
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | Manner Plastics, L.P. |
| Trademark: | Manner Flexible PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EoHW7c_Manner-Flexible-PVC-V969-NAT601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Recommended Applications: 105°C Low Smoke Jacket Compound . This product complies with the European Union Restriction on Hazardous Substances (RoHS) directive. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 to 1.50 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore D | 49 to 55 | ||
| Shore D, 15 sec | 41 to 47 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1 | 10.3 | MPa | ASTM D638 |
| Tensile Strength 2 | 14.5 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 250 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 4(136°C, 168 hr) | 6.0 | % | UL 1581 |
| Change in Ultimate Elongation in Air 5(136°C, 168 hr) | -18 | % | UL 1581 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -17.0 | °C | ASTM D746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 34 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Unaged Dumbbells: .03 inch |
| 2 . | Unaged Dumbbells: .03 inch |
| 3 . | Unaged Dumbbells: .03 inch |
| 4 . | Air Retention: .03 inch |
| 5 . | Air Retention: .03 inch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA610 A6G7301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 610 | Shandong PA610 |
| COPYLENE® CH090 | Phillips 66 | PP Homopolymer | COPYLENE® |
| DOMAMID® A1-001-N1-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| Hipolyene 8515 TY | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Hostalen PP XN112-I | LyondellBasell Industries | PP Random Copolymer | Hostalen |