Alathon® ETP H4262
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® ETP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EnxM8P_Alathon-ETP-H4262.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alathon H4262 is a high-flow resin that exhibits very good cold temperature impact performance, optimum processing and thermal stability, with good color and organoleptic properties. Typical customer applications include rigid food packaging such as four, five and six-quart ice cream containers produced at high speeds in fast-cycling, multi-cavity stack molds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.942 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 to 0.63 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) | 62 | g/10 min | ASTM D1238 |
| Spiral Flow | 47.5 | cm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 1010 | MPa | |
| 1% Secant | 798 | MPa | |
| Tensile Elongation 2(Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus 3 | ASTM D790 | ||
| -- | 971 | MPa | |
| 1% Secant | 840 | MPa | |
| 2% Secant | 716 | MPa | |
| Flexural Strength 4(Break) | 18.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 62.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 116 | °C | ASTM D1525 |
| Peak Melting Temperature | 125 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 113 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 246 | °C | |
| Cylinder Zone 2 Temp. | 246 | °C | |
| Cylinder Zone 3 Temp. | 243 | °C | |
| Cylinder Zone 4 Temp. | 232 | °C | |
| Cylinder Zone 5 Temp. | 232 | °C | |
| Adapter Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | 13 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer PBT-11020-GFFR | Polylink Polymers (India) Ltd. | PBT | Polylink Polymer |
| Sylvin RP 29001 Grey 9573 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VENELENE® 8407APUV | Poliolefinas Internacionales, C.A. (Polinter) | MDPE | VENELENE® |
| FAINGUM 6510 | Fainplast Compounds S.r.l | PVC, Unspecified | FAINGUM |
| Generic PC - Carbon Fiber | Generic | PC | Generic |