RTP 200 TFE 2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EnwRbd_RTP-200-TFE-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.4 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.5 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength | 107 | MPa | ASTM D790 |
| Compressive Strength | 33.8 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 640 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 188 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 71.1 | °C | ASTM D648 |
| CLTE - Flow | 7.9E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 24 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.010 | ASTM D150 | |
| Arc Resistance | 135 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammability, UL 94, was tested in accordance with RTP test standards.Tensile Elongation @ Yield, ASTM D-638: >10%Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 18mil/in.Flammability, ASTM D-635: B in/min. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 274 - 288 | °C | |
| Middle Temperature | 274 - 288 | °C | |
| Front Temperature | 274 - 288 | °C | |
| Mold Temperature | 65.6 - 107 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AVP™ TLL80CU | SABIC Innovative Plastics | PC | AVP™ |
| Fainplast PVC PG 83 | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| Hifax TRS 260P | LyondellBasell Industries | TPO (POE) | Hifax |
| Karina COMP. PVC CRYSTAL -E 74/240-D-IS-SD-TR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom ERC 161N G21259 | LyondellBasell Industries | PP Copolymer | Hostacom |