Reny® F34S
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EnGWrT_Reny-F34S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® F34S is a Polyarylamide (PARA) material filled with 30% whisker. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® F34S are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.59 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.59 | % | |
| Water Absorption (Saturation, 23°C) | 0.23 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 102 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2 |
| Flexural Modulus | 12300 | MPa | ISO 178 |
| Flexural Stress | 217 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.4 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 206 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 280 | °C | |
| Middle Temperature | 285 | °C | |
| Front Temperature | 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 80.0 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ad-Tech Urethanes UC-4750 | Ad-Tech Plastic Systems Corp. | TSU | Ad-Tech Urethanes |
| LNP™ LUBRICOMP™ RL003 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| Pinnacle PP 5135C3 | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |
| Plenco 07200 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |
| Teldene® H26ML | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |