CastForm™ PS

Category:	PS (Specialty) , Specialty Polystyrene
Manufacturer:	3D Systems
Trademark:	CastForm™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Ek7zUU_CastForm-PS.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

A styrene-based, expendable pattern casting material, compatible with most standard foundry processes.

Applications

Create patterns directly rather than through indirect methods

Complex investment casting patterns

Reactive metals like titanium

Low melt-temperature metals such as aluminum, magnesium and zinc

Ferrous and non-ferrous metals

Economic, low-volume production castings without tooling

Smaller parts can be joined to create very large patterns

Sacrificial, expendable patterns

Features

Functions like foundry wax and is "foundry friendly"

Low residual ash content (less than 0.02%)

Short burnout cycle

Easy-to-process plastic

Good plastic powder recycle characteristics

Benefits

Create complex patterns without welds or joints

Reduce lead times resulting in faster time-to-market

Compatible with autoclaves, low-temperature furnaces, and vacuum plaster casting methods

Easy to assemble and repair patterns

Rapidly test new designs in iterative process

General Information
Features	Clean/High Purity Good Processability
Uses	Mold Making Molds/Dies/Tools Patterns Prototyping
Processing Method	3D Printing, Laser Sintering/Melting

Physical	Nominal Value	Unit	Test Method
Specific Gravity
-- ¹	0.860	g/cm³	ASTM D792
-- ²	0.460	g/cm³	ASTM D4164
Water Absorption (Equilibrium, 20°C, 65% RH)	0.060	%	ASTM D570
Ash Content	0.020	%	ASTM D482

Flammability	Nominal Value	Unit
Flash Point - Cleveland Open Cup
-- ³	350	°C
-- ⁴	> 200	°C

Additional Information	Nominal Value	Unit
Auto-ignition ⁵	410	°C
Upward Surface ⁶
After Polishing	3.0	µm
As Processed	13.0	µm

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1600	MPa	ASTM D638
Tensile Strength (Ultimate)	2.84	MPa	ASTM D638

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	< 11	J/m	ASTM D256
Unnotched Izod Impact	14	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	89.0	°C	ASTM D3418
Melting Temperature ⁷	> 63.0	°C

Note Message
1 .	20°C
2 .	Tap
3 .	Polystyrene
4 .	Wax
5 .	Polystyrene
6 .	Mitutoyo Surftest-402
7 .	Wax

Resin Grade	Manufacturer	Category	Trademark
Mirathane™ E265	Miracll Chemicals Co., Ltd.	TPU-Polyester	Mirathane™
Sarlink® TPV 2464	Teknor Apex Company	TPV	Sarlink® TPV
Nanjing Hongrui PA66 A3010	Nanjing Hongrui Engineering Plastics Co., Ltd.	Nylon 66	Nanjing Hongrui PA66
Next Nylon 6 Industrial Series NX-02ABK	Next Polymers Ltd.	Nylon 6	Next Nylon 6 Industrial Series
Epoxies, Ect. 10-3005	Epoxies, Etc.	Epoxy	Epoxies, Ect.