Terluran® EHI-4
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Terluran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eitagh_Terluran-EHI-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Terluran® EHI-4 is a low flow, high impact extrusion grade with super high gloss and superior surface aesthetics. Styrolution's Terluran® EHI-4 is intended for mono or multilayer sheet making it a perfect fit for capping with our weatherable Luran® S ASA. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 39.2 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 3.2 | % | ASTM D638 |
| Fracture, 23°C | 19 | % | ASTM D638 |
| Flexural Modulus | 1780 | MPa | ASTM D790 |
| Flexural Strength (5.0% Strain) | 0.386 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 96 | J/m | ASTM D256 |
| 23°C | 410 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| Peak Force | 27.0 | J | ASTM D3763 |
| Total Energy | 42.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 95.6 | °C | ASTM D648 |
| Vicat Softening Temperature | 99.4 | °C | ISO 306/A50 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 100 | ASTM D523 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Melt Temperature | 218 - 260 | °C |
| Extrusion instructions |
|---|
| Suggested Max. Regrind: 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G30 291 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| ACCUTECH™ HP0334C10L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Boltaron 4005 | Boltaron Performance Products | PVC, Unspecified | Boltaron |
| Dialon 1015GF20V0 | DTR S.r.l. (Develop Thermoplastic Resins) | PC | Dialon |
| Lupoy® GN5001RFT | LG Chem Ltd. | PC+ABS | Lupoy® |