Propafilm™ RD140
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EiiMXh_Propafilm-RD140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Differentially Barrier Coated Film Biaxially oriented polypropylene (BOPP) film coated on one side with an aqueous dispersion of polyvinylidene chloride (PVdC) copolymer, the other side coated with an aqueous acrylic dispersion. RD125/140/160 are recommended for use in plain and printed form for overwrapping and for medium to large packages on form-fill-seal machines. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 121°C, 1 min | 4.0 | % | |
| Flow : 129°C, 1 min | 7.0 | % | |
| Across Flow : 129°C, 1 min | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.25 | ||
| vs. Itself - Static, Outside/Outside | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 3600 | µm | |
| Seal Strength | Internal Method | ||
| -- 1 | 0.15 | N/mm | |
| -- 2 | 0.15 | N/mm | |
| Seal Initiation Temperature | Internal Method | ||
| -- 3 | 104 to 146 | °C | |
| -- 4 | 85.0 to 146 | °C | |
| Oxygen Permeability (25°C, 0% RH) | 0.74 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 3.6 | g/m²/24 hr | ASTM F1770 |
| Yield | 30.1 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 100 | ASTM D2457 | |
| Haze 5 | 2.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | PVdC/PVdC; 265°F; 2secs; 15psi |
| 2 . | Acrylic/Acrylic; 265°F; 2secs; 15psi |
| 3 . | PVdC/PVdC; 2secs; 15psi |
| 4 . | Acrylic/Acrylic; 2secs; 15psi |
| 5 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT HI1003F | Sincerity Australia Pty Ltd. | PC+PBT | Sindustris PBT |
| Nanjing Hongrui PP P1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| FLEXCHEM™ 6552 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| LUVOCOM® 19-8365 | Lehmann & Voss & Co. | Nylon 46 | LUVOCOM® |
| Sylvin 9077-82C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |