AKROMID® B3 GFM 10/20 1 grey (4561)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EiTHp7_AKROMID-B3-GFM-10-20-1-grey-4561-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GFM 10/20 1 grey (4561) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised Polyamid 6 with good surface and dimensional stability Applications are optical attractive engine covers in the automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.38 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5500 | MPa | ISO 178 |
| Flexural Stress 2 | 165 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 5.6 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.3 | kJ/m² | |
| 23°C | 3.7 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 43 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 178 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 55.0 | °C | ISO 75-2/C |
| Melting Temperature 4 | 222 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx F662E43 | The Matrixx Group, Inc. | Nylon 66 | Matrixx |
| Stanyl® SC50 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Moplen EP240P | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| ACCUTECH™ HP0336G25M5CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Kuraray Poval® PVA 105 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |