INNOPOL® CS 2-5840 GB is a 40 % glass-bead filled polypropylene block-copolymer compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 2-5840 GB is recommended for producing injection moulded products, where the required properties are good stiffness besides dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.95 | % | ISO 294-4 |
| Flow direction | 1.1 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/2 |
| Tensile Stress (Yield) | 17.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.3 | kJ/m² | ISO 179/1eA |
| 23°C | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 16 | kJ/m² | ISO 179/1eU |
| 23°C | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 240 | °C | |
| Middle Temperature | 190 - 240 | °C | |
| Front Temperature | 190 - 240 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 50 - 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman ABS/PC FR380 | Shuman Plastics, Inc. | PC+ABS | Shuman ABS/PC |
| Sylvin 86001-75 Clear Yellow 4183 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Tenopom® POM B3 M3 NTLA014 PR301 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| Ferro PP TPP20AE54WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Globalprene® 3566 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |