ESENTTIA 18H86
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polipropileno del Caribe S.A. |
| Trademark: | ESENTTIA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eh2Etr_ESENTTIA-18H86.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characteristics: Medium melt flow rate Homopolymer polypropylene with high cleanness and stable processability, good tenacity/elongation balance, gas fading resistant, excellent whiteness. Recommended for: Staple fibers for carpets, blankets and filters, CF and BCF process for ropes, cords, rugs and carpets, general purpose injection molding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 17 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, 3.20 mm, Injection Molded) | 35.2 | MPa | ASTM D638 |
| Tensile Elongation 3(Yield, 3.20 mm, Injection Molded) | 9.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 4(3.20 mm, Injection Molded) | 1520 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 32 | J/m | ASTM D256A |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 6011-75A | RTP Company | TPE | RTP |
| ULTEM™ AUT230 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Latene® EP 7-V2 | LATI S.p.A. | PP Copolymer | Latene® EP |
| LEXAN™ IR2840 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Karina GRAY PVC COMPOUND 702-DA-18/406-BZ-AS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |