AKROMID® B3 GF 50 4 RM-M black (3221)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EgdKkH_AKROMID-B3-GF-50-4-RM-M-black-3221-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 50 4 RM-M black (3221) is a 50% glass fibre reinforced, chemical stabilised polyamide 6 with low humidity absorption and very good surface finish. Applications are housings and other dimensional stable parts in the automotive and electronic industry demanding high resistance against CaCl2-solvents, as well as a very good surface. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.60 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 50.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.30 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.2 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 50 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 280 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16500 | 13000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 210 | 160 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 16800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 320 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 16 | 20 | kJ/m² | |
| 23°C | 20 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 60 | kJ/m² | |
| 23°C | 65 | 65 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 165 | -- | °C | ISO 75-2/C |
| Melting Temperature 3 | 225 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumiflex® QE QE131ATH | Mitsubishi Chemical Corporation | TES | Sumiflex® QE |
| Monprene® CE-22968 | Teknor Apex Company | TPE | Monprene® |
| Viprene™ G65A-32U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| Wondel® B BN0 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 6 | Wondel® B |
| Pearlbond™ ECO D590 | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlbond™ ECO |