Beetle INJC
| Category: | Urea Formald , Urea Formaldehyde |
| Manufacturer: | BIP (Oldbury) Limited |
| Trademark: | Beetle |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EgWvwI_Beetle-INJC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Material suitable for a wide range of household articles such as Electrical accessories. Compared to standard Injection urea, INJC offers an improved stability for mouldings exposed to elevated temperatures. Its lower viscosity gives improved mould filling characteristics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | ||
| -- 1 | 0.73 | % | |
| -- 2 | 0.80 | % | |
| Water Absorption | ISO 62 | ||
| Cold 3 | 52.0 | mg | |
| Hot 4 | 305.0 | mg | |
| Post Shrinkage | ISO 2577 | ||
| -- 5 | 0.50 | % | |
| -- 6 | 0.47 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Martens Temperature | 115 | °C | DIN 43458 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Stress | 86.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 1.8 | kJ/m² | ISO 180/C |
| Unnotched Izod Impact Strength | 9.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 120 | °C | ISO 75-2/Ae |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | IEC 60243-1 | ||
| -- 7 | 9.0 | kV/mm | |
| -- 8 | 7.0 | kV/mm | |
| Comparative Tracking Index | > 600 | V | IEC 60167 |
| Note Message | |
|---|---|
| 1 . | Preheated powder |
| 2 . | Cold powder |
| 3 . | 24 hr @ 23°C |
| 4 . | 30 min @ 100°C |
| 5 . | Cold powder |
| 6 . | (48 hr) Preheated powder |
| 7 . | (90°C) Preheated powder |
| 8 . | Cold powder |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPUCO® TPUE-E98 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| ExxonMobil™ PP4712E1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| HiFill® PA6/6 GF60 IM HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Sylvin 802-90 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen RP348N | LyondellBasell Industries | PP Random Copolymer | Moplen |