Niplene F15 AGR
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niplene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EgRAFF_Niplene-F15-AGR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer, reinforced with 15% glass fibre chemically coupled to the polymeric matrix |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 to 0.80 | % | |
| Across Flow | 0.50 to 1.0 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus 3 | 3500 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-20°C, 3.20 mm) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648 |
| Vicat Softening Temperature | 135 | °C | ASTM D1525 5 |
| CLTE - Flow (23 to 55°C) | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 60 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.0 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENYL UG307 - 8139 | AD majoris | Nylon 66 | VENYL |
| UBESTA XPA 9063 X1 | UBE Engineering Plastics, S.A. | Nylon 12 Elast | UBESTA |
| Grilamid® XE 4180 black 9992 | EMS-GRIVORY | Nylon 1010 | Grilamid® |
| ADVANCENE™ EM-3405-UVH | ETHYDCO | MDPE | ADVANCENE™ |
| OTECH TPO OTR9088 - Gasket | OTECH Corporation | TPE | OTECH TPO |