SEPAZ™ C130M
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | SEPAZ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EgGYx6_SEPAZ-C130M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEPAZ™ C130M is a Liquid Crystal Polymer (LCP) product filled with 30% mineral. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.63 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 0.0 | % | |
| Across Flow | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 127 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 9610 | MPa | ASTM D790 |
| Flexural Strength | 127 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 239 | °C | ASTM D648 |
| Peak Melting Temperature | 335 | °C | ASTM D2133 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 26 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.20 | ASTM D150 | |
| Dissipation Factor | 0.028 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 350 to 360 | °C | |
| Mold Temperature | 30.0 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 90-A472R-75-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Hifax TYC 258P | LyondellBasell Industries | PP Copolymer | Hifax |
| Karina RED COLOR CONCENTRATE 42/55-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ DSL229 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| ORIENTENE FM 10 | Oriental Petrochemical Company | PP Homopolymer | ORIENTENE |