RTP 1378 CL
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EgE9KT_RTP-1378-CL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber Reinforced - PTFE Lubricated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11700 | MPa | ASTM D638 |
| Tensile Strength | 131 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 480 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 302 to 343 | °C | |
| Mold Temperature | 135 to 177 | °C | |
| Injection Pressure | 82.7 to 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trexprene® A55NI-HF | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Elexar® EL-8730B | Teknor Apex Company | TPE | Elexar® |
| Hifax PPU X9067HS UV | LyondellBasell Industries | PP Copolymer | Hifax |
| Plaslube® PA6/6 ML2 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| POCAN® B 3233 HR 000000 | LANXESS GmbH | PBT | POCAN® |