LubriOne™ SF-000/25BZ-15T bronze
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EgE4QX_LubriOne-SF-000-25BZ-15T-bronze.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.85 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.2 to 1.6 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2500 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 3200 | MPa | ASTM D790 |
| Flexural Strength | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 16 | kJ/m² | ISO 179 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Mold Temperature | 130 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9860M | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Ranger PBT PBT-201-G30 272 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Asaprene™ T-411 | AKelastomers | SBS | Asaprene™ |
| CompaDur® 121 GF 30 HR natural (051) | DimeLika Plast GmbH | PBT | CompaDur® |
| Elvacite® 2044 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |