Ultramid® B3UGM210
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eg47u8_Ultramid-B3UGM210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Halogen- and phosphorus-free injection molding grade with very high rigidity, low smoke density and outstanding electrical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.67 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.75 | -- | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 25.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.0 - 1.4 | -- | % | ISO 62 |
| Mold shrinkage- Test box (1.50 mm) | 0.50 | -- | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Conventional Index of Toxicity - 25 kW/m² | 0.400 | -- | ISO 5659-2 | |
| Fire Performance - UL94+HAI+HWI 1 | > 750.0 | -- | µm | UL 746C |
| French Railway Standard - fire and smoke classification | I3 / F2 | -- | NF F16-101 | |
| Smoke density- DS (max, 20 min), 25 kW/m² | 10 | -- | ISO 5659-2 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Hot Wire Test (> 750.0 µm) | 2.00 | -- | ASTM D3874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Screw Speed | mm/sec |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 110 | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.8 | 2.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 30 | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 195 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| RTI Elec (1.50 mm) | 130 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 4.50 | 5.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | 0.050 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | V-2 | -- | UL 94 | |
| > 1.50 mm | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | > 45 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Hopper Temperature | 80.0 | °C | |
| Rear Temperature | 280 | °C | |
| Middle Temperature | 290 | °C | |
| Front Temperature | 300 | °C | |
| Nozzle Temperature | 300 | °C | |
| Processing (Melt) Temp | 290 - 310 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Injection instructions |
|---|
| Residence time : <10 min |
| Note Message | |
|---|---|
| 1 . | For Electrical Insulation/Barrier with close proximity (< 0,8 mm) to uninsulated live parts according to UL 746C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Devcon Zip Patch | Devcon | Epoxy | Devcon |
| Fainplast PVC RE 330 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Jiangsu Sinarise JO9531 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Karina CLEAR PVC COMPOUND 80/268-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina PINK PVC -E TR-600N39/381-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |