C-Clear™ K7060
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | C-Clear™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eg3KGA_C-Clear-K7060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kumhosunny C-Clear™ K7060 is heat resistance ABS with low VOC ,high rigidity , toughness and good UV-stability . |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.40 to 0.70 | % | ISO 294-4 |
| VOC Content - Condition: 120°C*5h | < 18.0 | µgC/g | VDA 277 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging - Condition: 100°C*18h | < 2.0 | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ethylbenzene Emissions - Condition: 120°C*5h | < 8.00 | µg/g | VDA 277 |
| Odor | VDA 270 | ||
| Condition: 23°C*24h | Grade 2 | ||
| Condition: 40°C*24h | Grade 3 | ||
| Condition: 80°C*2h | Grade 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 12 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Flexural Stress 2 | 62.0 | MPa | ISO 178 |
| Poisson's Ratio 3 | 0.40 | ISO 527 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 4 | ISO 180 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Unnotched Izod Impact Strength 5(23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 113 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 250 to 270 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 1 mm/min |
| 4 . | Condition: 5.5 J |
| 5 . | Condition: 5.5 J |
| 6 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210M40 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Nypol® PA A3 G25 PRTA011 NR306 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Baydur® 426 IMR (Continuous Filament Mat) | Covestro - PUR | PUR-MDI | Baydur® |
| Hostaform® C 27021 XAP | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| HyTemp® 4451CG | Zeon Chemicals L.P. | Acrylic, Unspecified | HyTemp® |