Durethan® AKV 35 XTS1 901510
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EfXEv7_DurethanAKV35XTS1901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 35% glass fibers, injection molding, heat-aging stabilized, notably high heat-aging stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.41 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.90 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.15 | -- | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 0.35 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.050 | -- | % | ISO 2577 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10700 | 6800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 185 | 105 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.2 | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 10100 | 6200 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | 280 | 140 | MPa | ISO 178/A |
| 23°C 6 | 280 | 180 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.5 | 5.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | ISO 1874 - PA 66, GHR, 14-110, GF35 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 75 | 85 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | 10 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 65 | 70 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 235 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 261 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 9.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 504P | SABIC Americas, Inc. | PP Homopolymer | SABIC® PP |
| SLOVALEN® PC 82 T 30 | Plastcom | PP, Unspecified | SLOVALEN® |
| Sylvin 7833-95C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Enviramid® N2335HL BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |
| Osterlene® PPC-20-NB | Osterman & Company | PP Impact Copolymer | Osterlene® |