Infino NH-3402F
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EfURgF_Infino-NH-3402F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/GF material with 40% GF reinforcement that can be applied to printer LSU |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 33 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.20 mm | 0.11 to 0.13 | % | |
| Across Flow : 3.20 mm | 0.14 to 0.17 | % | |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9800 | MPa | ASTM D638 |
| -- | 10000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 140 | MPa | ASTM D638 |
| Yield | 184 | MPa | ISO 527-2/50 |
| Break 3 | 170 | MPa | ASTM D638 |
| Break | 180 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 3.2 | % | ASTM D638 |
| Break | 3.2 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 11000 | MPa | ASTM D790 |
| -- 6 | 12000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 180 | MPa | ASTM D790 |
| -- 8 | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 17 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 110 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 98 | J/m | ASTM D256 |
| 23°C 10 | 16 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 117 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 122 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 114 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 118 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.00 mm | V-1 | ||
| 2.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Pressure | 68.6 to 226 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA6 A1G6304 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6 | Shandong PA6 |
| THERMOLAST® K TF4CGN (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| 3M™ Dyneon™ Fluoroplastic PFA FLEX8515UHPZ | 3M Advanced Materials Division | PFA | 3M™ Dyneon™ Fluoroplastic |
| Koylene SR20NS | Reliance Industries Limited | PP Random Copolymer | Koylene |
| LNP™ THERMOCOMP™ WF006H compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |