Glass-fibre reinforced diallyl phthalate moulding compound free from halogens Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensional stability even under severe environmental conditions Primary application(s): Pin and socket connectors, Spools, Potentiometers, Switches This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
Uses |
|
Agency Ratings |
|
RoHS Compliance |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.90 to 2.10 | g/cm³ | ISO 1183 |
Apparent Density | 0.75 to 0.90 | g/cm³ | ISO 60 |
Molding Shrinkage - Flow | ISO 2577 | ||
-- 1 | 0.50 to 0.60 | % | |
-- 2 | 0.30 to 0.40 | % | |
Water Absorption (23°C, 24 hr) | < 0.20 | % | ISO 62 |
Post Shrinkage 3 | < 0.050 | % | ISO 2577 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | ISO 527-2 | ||
Compression Molded | 6000 to 9000 | MPa | |
Injection Molded | 9000 to 11000 | MPa | |
Tensile Stress | ISO 527-2 | ||
Compression Molded | 35.0 to 60.0 | MPa | |
Injection Molded | 40.0 to 70.0 | MPa | |
Flexural Modulus | ISO 178 | ||
Compression Molded | 8000 to 12000 | MPa | |
Injection Molded | 13000 to 16000 | MPa | |
Flexural Stress | ISO 178 | ||
Compression Molded | 80.0 to 100 | MPa | |
Injection Molded | 100 to 140 | MPa | |
Compressive Stress | 150 to 200 | MPa | ISO 604 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength | ISO 179/1eA | ||
Compression Molded | 2.5 to 3.5 | kJ/m² | |
Injection Molded | 3.5 to 5.0 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
Compression Molded | 5.0 to 10 | kJ/m² | |
Injection Molded | 8.0 to 11 | kJ/m² |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature | |||
1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
8.0 MPa, Unannealed | > 180 | °C | ISO 75-2/C |
CLTE - Flow (50 to 100°C) | 5.0E-6 to 1.0E-5 | cm/cm/°C | ISO 11359-2 |
Thermal Conductivity | 0.90 to 1.1 | W/m/K | ASTM E1461 |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Surface Resistivity | 1.0E+14 to 1.0E+15 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+14 to 1.0E+15 | ohms·cm | IEC 60093 |
Electric Strength | 35 to 40 | kV/mm | IEC 60243-1 |
Relative Permittivity | IEC 60250 | ||
100 Hz | 5.00 4.50 | ||
1 MHz | 4.50 4.00 | ||
Dissipation Factor | IEC 60250 | ||
100 Hz | 0.010 to 0.030 | ||
1 MHz | 0.010 to 0.030 | ||
Arc Resistance | PLC 4 | ASTM D495 | |
Comparative Tracking Index | 600 | V | IEC 60112 |
Flammability | Nominal Value | Unit | Test Method |
---|---|---|---|
Flame Rating (0.800 mm, Tested by RASCHIG) | V-0 | UL 94 | |
Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
Glow Wire Ignition Temperature | 930 | °C | IEC 60695-2-13 |
Note Message | |
---|---|
1 . | Compression Molded |
2 . | Injection Molded |
3 . | 168 h / 110°C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Sanren EVA 12/0.5 | SINOPEC Shanghai Petrochemical Co. Ltd. | EVA | Sanren |
VYTEEN PC 135 | Lavergne Group | PC | VYTEEN |
Nipol® 1562 | Zeon Corporation | Latex | Nipol® |
Fixmaster Flex 80 Putty | Loctite® | PUR, Unspecified | Fixmaster |
Escorene™ Ultra UL 00112 | ExxonMobil Chemical | EVA | Escorene™ Ultra |