Infino NH-8310
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ef6Z18_Infino-NH-8310.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino NH-8310 is a Polyphenylene Ether (PPE) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 14 | g/10 min | ASTM D1238, ISO 1133 |
| Ash Content | 34 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 110 | MPa | ASTM D638 |
| Yield | 112 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 8300 | MPa | ASTM D790 |
| -- 3 | 8670 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 140 | MPa | ASTM D790 |
| -- 5 | 143 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 134 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 137 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 4.00 mm | 127 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 131 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 132 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 3.00 mm | V-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 290 to 300 | °C | |
| Nozzle Temperature | 300 | °C | |
| Mold Temperature | 50.0 to 100 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 30S5401 | The Matrixx Group, Inc. | PBT | Matrixx |
| TRIBOCOMP® PA66 TS0 | EPIC Polymers | Nylon 66 | TRIBOCOMP® |
| Xuchuan A-9007/B-6088 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Panlite® LN-2250Z | TEIJIN LIMITED | PC | Panlite® |
| POLYabs HF0 | Polykemi AB | ABS | POLYabs |