RTP 6011-55A Z
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ee0qVz_RTP-6011-55A-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Wet-Grip Compound - 55 Shore A - FDA Compliant Ingrediants |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 58 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 8.27 | MPa | ASTM D412 |
| Tensile Elongation 2(Break) | 1100 | % | ASTM D412 |
| Tear Strength 3 | 28.0 | kN/m | ASTM D624 |
| Compression Set 4(70°C, 22 hr) | 48 | % | ASTM D395B |
| Additional Information |
|---|
| Peel Strength, ISO 813, 90°, 20 in/min, PP, Interface Failure: 15 pliWet-Grip Compound |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 177 - 191 | °C | |
| Mold Temperature | 21.1 - 37.8 | °C | |
| Injection Pressure | 3.45 - 5.17 | MPa |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | C mould |
| 4 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax PL505 | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |
| STYRON™ 660 | Trinseo | PS (GPPS) | STYRON™ |
| Iupital® FT2020 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| LNP™ THERMOCOMP™ RF003ES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| LubriOne™ NN-30GF/15T Black | PolyOne Corporation | Nylon 66 | LubriOne™ |