SABIC® PP 575P
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EbXGHq_SABIC-PP-575P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This grade combines a high stiffness with moderate impact strength. It is suitable for production of complex articles with long flow paths and thin walls. Typical applications are closures and garden furniture. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 111 | ASTM D785 | |
| Shore Hardness (Shore D) | 69 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1800 | MPa | ASTM D638 |
| -- | 1700 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 36.0 | MPa | ASTM D638 |
| Yield | 36.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 9.0 | % | ASTM D638 |
| Yield | 9.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 25 | J/m | ASTM D256A |
| 23°C | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 90.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 95.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2607 | Covestro - Polycarbonates | PC | Makrolon® |
| Radilon® A 42K 100 M NAT | Radici Plastics | Nylon 66 | Radilon® |
| Ekatal® H 12 | Sattler KunststoffWerk GmbH | Acetal (POM) Copolymer | Ekatal® |
| LOXIM 330 12 V0 | LOXIM Industries Private Limited | Nylon 6 | LOXIM |
| Petrotene® PP A3 G20 BRC0001 PH321 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |