A Skived PTFE film that is produced from a modified homopolymer PTFE resin containing <1% of a fully fluorinated comonomer. The incorporation of the comonomer yields a material with improved electrical and physical properties. This film can be thermally fused to itself. The modified homopolymer resin exhibits chemical resistance equivalent to that of a standard homopolymer PTFE. It's tensile strength is approximately 10% higher and the elongation is approximately 30% higher than for a standard homopolymer PTFE. With its ability to be heat fused, this film finds applications in the convoluted PTFE hose industry as a inner liner material.

Message

A Skived PTFE film that is produced from a modified homopolymer PTFE resin containing <1% of a fully fluorinated comonomer. The incorporation of the comonomer yields a material with improved electrical and physical properties. This film can be thermally fused to itself. The modified homopolymer resin exhibits chemical resistance equivalent to that of a standard homopolymer PTFE. It's tensile strength is approximately 10% higher and the elongation is approximately 30% higher than for a standard homopolymer PTFE.

With its ability to be heat fused, this film finds applications in the convoluted PTFE hose industry as a inner liner material.

General Information
Features	Good Chemical Resistance Good Electrical Properties High Elongation High Tensile Strength Homopolymer
Uses	Film Hose Liners
Forms	Film

Physical	Nominal Value	Unit
Thickness	25.4 to 1020	nm

Additional Information	Nominal Value	Unit
Core ID	7.62	cm
Maximum Roll OD	356	mm
Width	6.35 to 1140	mm

Films	Nominal Value	Unit	Test Method
Tensile Strength - MD (Yield)	24.8	MPa	ASTM D882
Tensile Elongation - MD (Break)	250	%	ASTM D882

Thermal	Nominal Value	Unit
Continuous Use Temperature	260	°C

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	98	kV/mm	ASTM D149

Resin Grade	Manufacturer	Category	Trademark
SEPTON™ 1001	Kuraray Co., Ltd.	SEP	SEPTON™
Gallonprene® GP410-7501	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®
Laser+® C 9921 (F65A)	DAK Americas LLC	PET	Laser+®
Karina BLACK PVC COMPOUND 105800-48/1-B-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
LNP™ LUBRICOMP™ RN001 compound	SABIC Innovative Plastics Europe	Nylon 66	LNP™ LUBRICOMP™