LNP™ STAT-KON™ TX06488NTX1 compound
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EbEb6f_LNP-STAT-KON-TX06488NTX1-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON TX06488NTX1 is a compound based on Polyurethane resin containing Proprietary Filler(s). Added features of this grade are: Execllent Ductility, Electrically Conductive. Also known as: LNP* STAT-KON* Compound TX06488 Product reorder name: TX06488NTX1 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.80 to 1.0 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.67 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.89 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 65.0 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 19.0 | MPa | |
| Break | 18.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 390 | % | |
| Break | 390 | % | |
| Flexural Modulus 4(50.0 mm Span) | 63.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 39.8 | J | ASTM D3763 |
| -- | 41.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 23.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 5 | 23.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 23.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 6 | 23.0 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 80*10*4 mm |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tislamid® PA6 PA6 20 GFR FR | Tisan | Nylon 6 | Tislamid® PA6 |
| AKROMID® B3 GFM 10/20 1 grey (4561) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| ExxonMobil™ LLDPE LL 1004YB Wire & Cable | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Hostalen GM 9240 HT | LyondellBasell Industries | HDPE | Hostalen |
| Karina YELLOW PVC COMPOUND 550D02/101-AT-IS (MECESA) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |