ASTAMID™ MA3G3HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Eb6Nid_ASTAMID-MA3G3HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTAMID™ MA3G3HS is a 15% glass fibre reinforced and heat stabilised injection moulding grade of Polyamide 66 (PA 66) designed for general industrial applications requiring medium level of strength and rigidity. It has good chemical resistance, heat resistance and long term durability. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTAMID™ MA3EG7UV ]. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.23 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 6.5 | -- | % | ASTM D570 |
| Moisture Regain 1 | 2.0 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 115 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 2(3.20 mm) | 6000 | 4500 | MPa | ASTM D638 |
| Tensile Strength 3(3.20 mm) | 125 | 80.0 | MPa | ASTM D638 |
| Tensile Elongation 4(Break, 3.20 mm) | 3.0 | 9.0 | % | ASTM D638 |
| Flexural Modulus 5(3.20 mm) | 5700 | 4100 | MPa | ASTM D790 |
| Flexural Strength 6(3.20 mm) | 240 | 170 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 65 | 110 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 240 | -- | °C | ASTM D648 |
| CLTE - Flow | 2.2E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 280 - 295 | °C | |
| Front Temperature | 290 - 300 | °C | |
| Processing (Melt) Temp | 260 - 285 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Pressure | 60.0 - 130 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 3.0 - 5.0 | kN/cm² |
| Injection instructions |
|---|
| Drying Time (Opened Bag): >12 hr |
| Note Message | |
|---|---|
| 1 . | 65% RH |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® PXPO103 | Tekni-Films, a div of Tekni-Plex | Film, Copolyester/PE/EVOH/PE | TEKNIFLEX® |
| Stanyl® TE250F6 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| MOSTEN MT 935 | UNIPETROL RPA | PP Random Copolymer | MOSTEN |
| Bergamid™ A700 G15 H W UF NC059 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Chiao Fu PA66 MD312LA10 | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |