Zytel® 70G25HSLR NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EaYvpc_Zytel-70G25HSLR-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% Glass Reinforced, Heat Stabilized, Hydrolysis Resistant, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 6.4 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.0 | -- | % | |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 260 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8400 | 6100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 180 | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 7.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | 7.0 | kJ/m² | |
| 23°C | 10 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 45 | kJ/m² | |
| 23°C | 60 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 261 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 252 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 80.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 257 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 3.3E-5 | -- | cm/cm/°C | |
| Transverse | 1.1E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Relative Permittivity (100 Hz) | 3.60 | -- | IEC 60250 | |
| Dissipation Factor (100 Hz) | 7.0E-3 | -- | IEC 60250 | |
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 26 | -- | mm/min | ISO 3795 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Density | 1.15 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2090 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.21 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Odor | 3.5 | -- | VDA 270 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound G3240U | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| Bayblend® FR3021 GR | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Chemlon® 102 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Grilamid® XE 4108 nat | EMS-GRIVORY | Nylon 6/12 | Grilamid® |
| Hifax BR 1149 A | LyondellBasell Industries | PP Impact Copolymer | Hifax |