Innothane® IE-3030
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EaSn9G_Innothane-IE-3030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-3030 is a rigid polyurethane formulated for hand-batch processing or vacuum cast methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA or TDI. It has excellent green strength yielding enhanced demold characteristics and also yields easy to paint surfaces requiring little preparation. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.06 | g/cm³ | |
| Hardener | 1.06 | g/cm³ | |
| Base Resin | 1.16 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.60 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1210 | MPa | ASTM D790 |
| Flexural Strength | 49.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 72.0 | °C | |
| 1.8 MPa, Unannealed | 65.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 92 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 10 to 20 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.075 | Pa·s | |
| 25°C 2 | 0.15 | Pa·s | |
| 25°C 3 | 0.45 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 2.8 to 3.8 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 to 75 | ASTM D2240 | |
| Tensile Modulus | 1140 | MPa | ASTM D638 |
| Tensile Strength | 34.1 | MPa | ASTM D638 |
| Tensile Elongation at Break | 24 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Prime Series NGF25-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Aero-Lite® ALSTDA.2001BG | Azdel, Inc. | PEI | Aero-Lite® |
| Gallonprene® GP540-8005 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| KumhoSunny PA/ABS HNB0225 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+Nylon | KumhoSunny PA/ABS |
| OmniTech™ ASA 407 HSV | OMNI Plastics, LLC | ASA | OmniTech™ |