Lavanta® 5120 BK 368
| Category: | HPP , High Performance Polyester |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Lavanta® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EaQCTG_Lavanta5120BK368.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lavanta® HPP 5120 is a 20% glass fiber reinforced, high-performance polyester (HPP) injection molding grade developed specifically for HB LED packaging applications that utilize surface mount technology. Key performance properties include easy processing, high stiffness and low moisture absorption, giving it excellent reliability for LEDs used in outdoor displays. -Black: 5120 BK368 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 1.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.057 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7280 | MPa | ISO 527-2 |
| Tensile Stress | 101 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2 |
| Flexural Modulus | 6360 | MPa | ISO 178 |
| Flexural Stress | 164 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 4.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 274 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 241 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : 50 to 100°C | 2.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : 150 to 200°C | 1.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : 200 to 250°C | 1.5E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 0 to 50°C | 7.2E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 50 to 100°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Horizontal : 100 to 150°C | 1.6E-4 | cm/cm/°C | ASTM E831 |
| Horizontal : 150 to 200°C | 1.6E-4 | cm/cm/°C | ASTM E831 |
| Horizontal : 200 to 250°C | 1.7E-4 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 280 - 290 | °C | |
| Front Temperature | 300 - 310 | °C | |
| Processing (Melt) Temp | 300 - 320 | °C | |
| Mold Temperature | 120 - 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 81005 | RTP Company | PBT | RTP |
| Resinoid 2016P | Resinoid Engineering Corporation | Phenolic | Resinoid |
| VENELENE® 2811 | Poliolefinas Internacionales, C.A. (Polinter) | HDPE | VENELENE® |
| Geon™ Vinyl Fittings 216A | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Fittings |
| INNOPOL® PP CS 2-5000 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |