OmniCarb™ PC08FR GF10
| Category: | PC , Polycarbonate |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniCarb™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EZgx8G_OmniCarb-PC08FR-GF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% Glass Reinforced, Flame Resistant Polycarbonate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 0.50 | % | |
| Across Flow | 0.10 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 12 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 143 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 135 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| 3.00 mm, Black | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 293 | °C | |
| Middle Temperature | 271 to 304 | °C | |
| Front Temperature | 271 to 304 | °C | |
| Nozzle Temperature | 271 to 304 | °C | |
| Processing (Melt) Temp | 271 to 304 | °C | |
| Mold Temperature | 48.9 to 104 | °C | |
| Back Pressure | 0.172 to 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC PP R3450 | LG Chem Ltd. | PP Random Copolymer | SEETEC PP |
| UNITIKA Nylon 66 B2040G50 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| Boltaron 3020 TruPrint | Boltaron Performance Products | PVC, Rigid | Boltaron |
| LNP™ THERMOTUF™ VF004S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |
| Sylvin 8925-85 Blue 8366 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |