HyFlex P021
| Category: | Copolyester , Copolyester |
| Manufacturer: | KMI Group, Inc. |
| Trademark: | HyFlex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EZ8CwN_HyFlexP021.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HyFlexP021 polymer is a modified co-polyester that exhibits elastomeric properties. HyFlexP021 can be melt spun into Fiber and Monofilament, and can also be extruded for other applications that require elastic properties in the final product. HyFlexP021 co-polyester needs to be dried to <50ppm moisture (110°C/-40°C d.pt. air/14+ hours) if processed on single screw extruder. Drying in dry nitrogen atmosphere is preferred. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Test Method | |
|---|---|---|---|
| Color b - Hunter Colorimeter | 14.0 - 28.0 | ||
| Color L - Hunter Colorimeter | 64.0 - 78.0 | ||
| Intrinsic viscosity- 0.1% Solution in M-cresol | 1.0 - 1.4 |
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 43 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 18.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 460 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 260 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | < 240 | °C | DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ARE-75A | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Ekalon® 14 E I | Sattler KunststoffWerk GmbH | PC | Ekalon® |
| Hylon® N2023STHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Later 4E61 | LATI S.p.A. | PBT | Later |
| Hostacom HRC 181L W92341 | LyondellBasell Industries | PP Homopolymer | Hostacom |