Terralene® WF 5525
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Terralene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EYZvYE_Terralene-WF-5525.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High desnity polyethylene with narrow molar mass distribution, containing a medium amount of wood fibers and functional additives. Recommended for the production of injection moulded articles. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 to 7.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1920 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 25.0 | MPa | |
| Break | 24.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | 7.0 | % | |
| Flexural Modulus | 1950 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 29.0 | MPa | ISO 178 |
| Flexural Strain at Break | No Break | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.6 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 12 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 130 to 145 | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Measured on injection moulded specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SE-400H | SHIN-A T&C | Epoxy | SHIN-A |
| Ateva® 1820 | Celanese EVA Performance Polymers | EVA | Ateva® |
| Edgetek™ AS-000/000 AS UV | PolyOne Corporation | ABS | Edgetek™ |
| Laprene® 8K1000A80 | SO.F.TER. SPA | SEBS | Laprene® |
| Iupital® F20-03 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |