Cleapact TS-50
| Category: | SBC , Styrene Butadiene Block Copolymer |
| Manufacturer: | DIC Corporation |
| Trademark: | Cleapact |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EYC7Va_Cleapact-TS-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Developed with our unique polymerization technology, Cleapact is a type of styrene copolymer resin that excels in the balance of transparency, shock-resistance and molding capacity. Products in this category have a variety of positive characteristics and meet diverse range of user needs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.70 | % | Internal Method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 71 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, Injection Molded) | 64.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 4.0 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 3450 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 104 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 2.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ISO 306 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Injection Molded) | 91.0 | % | JIS K7105 |
| Haze (Injection Molded) | 0.30 | % | JIS K7105 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 | °C | |
| Drying Time | 3.0 | hr |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 | °C | |
| Drying Time | 3.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ CRT6302 | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| UBESTA 3020 GX12 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Borlink™ LE0315-99 | Borealis AG | TP, Unspecified | Borlink™ |
| Axpoly® PP19 1021 | Axion Polymers | PP Homopolymer | Axpoly® |
| Karina IVORY PVC COMPOUND BTR-85/200-D-IS-BS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |