EPO-TEK® OG146-178
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EXf2Mt_EPO-TEK-OG146-178.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A fast UV cure epoxy with low viscosity Formerly 88-178 |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | 82.0 | °C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index | |||
| -- 1 | 1.509 | ||
| -- 2 | 1.535 | ||
| Transmittance (440 to 1680 nm) | > 98.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life 3 | 26 | wk |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 341 | °C | |
| Operating Temperature | |||
| Continuous | -55 to 175 | °C | |
| Intermittent | -55 to 275 | °C | |
| Weight Loss on Heating | |||
| 200°C | 0.38 | % | |
| 250°C | 0.82 | % | |
| 300°C | 2.9 | % |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | Clear/Transparent | ||
| Density | 1.08 | g/cm³ | |
| Viscosity 4(23°C) | 0.16 | Pa·s |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 82 |
| Note Message | |
|---|---|
| 1 . | 589 nm (uncured) |
| 2 . | 589 nm (cured) |
| 3 . | Refrigerated |
| 4 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| METLBOND® 1515-4 | Cytec Industries Inc. | Epoxy | METLBOND® |
| Silopren® LSR 2620 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Chiao Fu PA66 MD312G23 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Elastron® G G100.A85.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Lumid® GP2200B(W) | LG Chem Ltd. | Nylon 66 | Lumid® |