Fiberfil® PP-60/CC/30
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EXF6Tg_Fiberfil-PP-60-CC-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fiberfil® PP-60/CC/30 is a Polypropylene Homopolymer (PP Homopolymer) material filled with 30% calcium carbonate. It is available in North America. Primary attribute of Fiberfil® PP-60/CC/30: Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 1.1 | % | |
| 6.35 mm | 1.1 | % | |
| Water Absorption (24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2620 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 40 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 2450 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 41.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 121 | °C | |
| 1.8 MPa, Unannealed | 73.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PA66 EB130 | Guangdong Shunde Shunyan New Material Co., Ltd. | Nylon 66 | Sunny® |
| TUFNYL® RGF 15 GREY | SRF Ltd. | Nylon 66 | TUFNYL® |
| Ultramid® B3WG6 BK00564 BGVW | BASF Corporation | Nylon 6 | Ultramid® |
| Bergamid™ B700 G35 H Black | PolyOne Corporation | Nylon 6 | Bergamid™ |
| HIVOREX 2210J | Lotte Chemical Corporation | HDPE | HIVOREX |