Order Products : sales@su-jiao.com
Generic Nylon 46 - Glass Fiber
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EXEFnX_Generic-Nylon-46---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 46 - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.17 - 1.68 | g/cm³ | ASTM D792 |
| 23°C | 1.29 - 1.77 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.50 - 0.60 | % | ASTM D955 |
| 23°C | 0.27 - 1.3 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.90 - 2.6 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.2 - 3.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7990 - 16100 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Fracture, 23°C | 48.3 - 231 | MPa | ASTM D638 |
| Fracture, 23°C | 140 - 252 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.7 - 4.1 | % | ASTM D638 |
| Fracture, 23°C | 1.9 - 4.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 8180 - 11000 | MPa | ASTM D790 |
| 23°C | 7250 - 14100 | MPa | ISO 178 |
| Flexural Strength (23°C) | 96.5 - 317 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.7 - 18 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 34 - 100 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 95 - 120 | J/m | ASTM D256 |
| 23°C | 6.0 - 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 287 - 291 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 288 - 290 | °C | ISO 75-2/A |
| Melting Temperature | 295 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 1.8E-5 - 3.7E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.0E-5 - 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 3.9E-5 - 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 23°C | 1.0E+11 - 2.0E+14 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+14 - 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 22 - 28 | kV/mm | ASTM D149 |
| 23°C | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 297 - 409 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.1 | °C | |
| Drying Time | 3.0 - 7.2 | hr | |
| Suggested Max Moisture | 0.050 - 0.052 | % | |
| Rear Temperature | 295 - 300 | °C | |
| Middle Temperature | 299 - 318 | °C | |
| Front Temperature | 299 - 323 | °C | |
| Nozzle Temperature | 290 | °C | |
| Processing (Melt) Temp | 281 - 323 | °C | |
| Mold Temperature | 90.0 - 108 | °C | |
| Back Pressure | 0.172 - 6.00 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 46 - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NaturePlast PEVE 010 | NaturePlast | HDPE | NaturePlast |
| Braskem PP TI4150WR | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| Geon™ Vinyl Flexible C70U0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hylon® N1033HLFRA | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Sylvin 6203-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |